High Refractoriness Clinker Magnesia Chrome Brick Refractory Brick Prices
High chrome bricks use corundum and fused by chromic oxide and zirconium oxide as the main raw material, match with a variety of oxide powder additives, through numerical control intelligent hybrid configuration, molding, drying, in shuttle kiln high temperature burn becomes. High chrome brick have features of good thermal shock resistance, volume stability under high temperature, alkali slags resistance, and high refractoriness under load. high chrome refractory brick is mainly applied to line the sintering zone of the new dry processing of cement kilns and glass tank furnaces as checkers and the other industrial furnaces.
High Chrome Bricks Description
High chrome bricks is made of magnesia (MgO) and chromium oxide (Cr2O3) as the main ingredient, periclase and spinel as the main mineral components of refractory products. Such brick high refractoriness, high temperature strength, resistance to basic slag erosion resistance, excellent thermal stability, acidic slag also has some adaptability. The main raw material to manufacture high chrome refractory brick is sintered magnesia and chromite. Purity magnesia raw material to be as high as possible, the requirements of the chemical composition of chromite is: Cr2O3: 30 ~ 45%, CaO1.0 ~ 1.5%.
Properties of High Chrome Bricks
.High strength,
.Corrosion resistance,
.Erosion resistance,
.Excellent slag resistance,
.Good thermal shock stability.
Composition of High Chrome Bricks
High chrome bricks are mainly consist of Cr2O3, monoclinic zirconia and alumina powder. Therefore, the performance of high chromebricks is closely related to the performance of these substances. High chrome fire brick contains chromium hemitrioxide 30%, and high chrome brick is featured with acid and alkali slags resistance, and are mainly used in the isolation layer, and nonferrous smelting furnaces, etc.
High Chrome Bricks Manufacturing Process
High chrome refractory brick is made out of high quality magnesite and chrome ore fine charge mixture. According to different demands, adjust the content of Cr2O3, The product thermal stability and high temperature performance are satisfactory. High chrome bricks are widely used in the cement kiln and nonferrous metallurgical furnace etc.
Rongsheng Refractory High Chrome Bricks Specifications
Brand MgO % Cr2O3 % SiO2 % A.P. % BDg/cm3 CCS.MPa R.U.L ℃
LADBMGe-8A ≥74 ≥8 ≤1.5 ≤18 2.98 ≥40 1660
LADBMGe-8B ≥74 ≥8 ≤2.0 ≤18 2.98 ≥35 1600
LADBMGe-12A ≥66 ≥12 ≤1.5 ≤18 3.1 ≥40 1660
LADBMGe-12B ≥66 ≥12 ≤2.0 ≤18 3.1 ≥35 1600
LADBMGe-16A ≥60 ≥16 ≤1.5 ≤18 3.15 ≥40 1660
LADBMGe-16B ≥60 ≥16 ≤2.0 ≤18 3.15 ≥35 1600
Application of High Chrome Bricks
High chrome bricks can be used in the metallurgical industry, architectural material industry, and other non ferrous smelting furnace, etc. and also can be applied to line the sintering zone of the new dry processing of cement kilns and glass tank furnaces as checkers and the other industrial furnaces.